Bellofram Dense (Solid Silicone) Products
Our multiple lines, extensive expertise in custom formulations, and tool-making capabilities allow us to produce dense silicone across an almost limitless range. Our dense compounds meet the ASTM D 2000 specifications, ranging in hardness from 30 Shore “A” to 80 Shore “A” durometer. Dense silicone compounds are also available in flame-retardant and NSF/ANSI 51 compliant versions. All silicone compounds are designed to exceed requirements of a wide range of industrial, aerospace, and MIL-specs.
Bellofram Dense Solid Silicone - Extruded
MATERIAL PROPERTIES OF BELLOFRAM HIGH TEAR AND FLEX RESISTANT SOLID SILICONES EXTRUDED PRODUCTS | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
SOLID SILICONE EXTRUDED PRODUCTS TO SPEC TO SPEC A-A-59588 CL3B, GR30, GR50 | ASTM D395 | Heat Age, 70 Hours @ +200°C (ASTM D573) | ASTM D2137 | ASTM D471 | ASTM D813 | ASTM D2632 | |||||||
SPEC SHEET DOWNLOAD | COMPOUND MODEL | DUROMETER, SHORE "A" | TENSILE STRENGTH min MPa (PSI) | ELONGATION % min. | TEAR RESISTANCE, kN/m (ppi) | COMPRESSION SET, 70 Hours @ +100°C | HARDNESS CHANGE | TENSILE CHANGE | ELONGATION CHANGE | BRITTLE POINT, min. °C (°F) | WATER IMMERSION, VOLUME CHANGE % | DeMATTIA FLEX, (1/2 inch max crack growth) | IMPACT RESILIENCE, min % |
![]() |
6305 | 30 ± 5 | 6.9 (1000) | 500 | 26.25 (150) | 25 | ± 5 | -20% | -35% | -70 (-94) | +5 | 500,000 cycles | 40 |
![]() |
6505 | 50 ± 5 | 8.28 (1200) | 500 | 26.25 (150) | 20 | ±10 | -25% | -30% | -70 (-94) | +5 | 140,000 cycles | 45 |
MATERIAL PROPERTIES OF BELLOFRAM SOLID SILICONE EXTRUDED PRODUCTS | |||||||
SPEC SHEET DOWNLOAD | COMPOUND MODEL | ASTM D2000-08 DESIGNATION | DUROMETER SHORE "A" | TENSILE (PSI) | HEAT AGE, 70 Hours @ +225 °C | OIL IMMERSION IRM 903 70 hrs @+150 °C | COMPRESSION SET, 22 Hours @ +175°C |
![]() |
6304 | ASTM D2000 M1GE305 | 30 ± 5 | 1175 | Change in Tensile Strength, ±30% Change in Elongation, -50% Change in Durometer, ±15 pts | Volume change, +63% | 28% |
![]() |
6404 | ASTM D2000 M1GE405 | 40 ± 5 | 1150 | Volume change, +61% | 42% | |
![]() |
6504 | ASTM D2000 M1GE505 | 50 ± 5 | 930 | Volume change, +59% | 61% | |
![]() |
6604 | ASTM D2000 M1GE605 | 60 ± 5 | 925 | Volume change, +46% | 33% | |
![]() |
6704 | ASTM D2000 M1GE705 | 70 ± 5 | 820 | Volume change, +41% | 42% | |
![]() |
6804 | ASTM D2000 M1GE805 | 80 ± 5 | 810 | Volume change, +35% | 40% |
MATERIAL PROPERTIES OF BELLOFRAM FLAME RETARDANT SOLID SILICONE EXTRUDED PRODUCTS | ||||||||
SPEC SHEET DOWNLOAD | COMPOUND MODEL | ASTM D2000-08 DESIGNATION | DUROMETER SHORE "A" | TENSILE MPa (PSI) | HEAT AGE, 70 Hours @ +225 °C | OIL IMMERSION IRM 903 70 hrs @+150 °C | COMPRESSION SET, 22 hrs @+175°C | MEETS BURN REQUIREMENTS OF UL 94 V-0 |
![]() |
6309 | ASTM D2000 M1GE305 | 30 ± 5 | 5 ( 725 ) | Change in Tensile Strength, ±30% Change in Elongation, -50% Change in Durometer, ±15 pts | Volume change, +80% | 50% max. | PASS |
![]() |
6409 | ASTM D2000 M1GE405 | 40 ± 5 | 50% max. | PASS | |||
![]() |
6509 | ASTM D2000 M1GE505 | 50 ± 5 | 70% max. | PASS | |||
![]() |
6609 | ASTM D2000 M1GE605 | 60 ± 5 | 70% max. | PASS | |||
![]() |
6709 | ASTM D2000 M1GE705 | 70 ± 5 | 50% max. | PASS | |||
![]() |
6809 | ASTM D2000 M1GE805 | 80 ± 5 | 50% max. | PASS |
MATERIAL PROPERTIES OF BELLOFRAM NSF/ANSI 51 CERTIFIED SOLID SILICONE EXTRUDED PRODUCTS | ||||||||
SPEC SHEET DOWNLOAD | COMPOUND MODEL | ASTM D2000-08 DESIGNATION | DUROMETER SHORE "A" | TENSILE (PSI) | HEAT AGE, 70 Hours @ +225 °C | OIL IMMERSION IRM 903 70 hrs @ +150 °C | COMPRESSION SET, 22 Hrs @+175°C | NSF/ANSI 51 CERTIFIED |
![]() |
6304-NSF | ASTM D2000 M1GE305 | 30 ± 5 | 1175 | Change in Tensile Strength, ±30% Change in Elongation, -50% Change in Durometer, ±15 pts | Volume change +63% | 28% | Yes |
![]() |
6404-NSF | ASTM D2000 M1GE405 | 40 ± 5 | 1150 | Volume change, +61% | 42% | Yes | |
![]() |
6504-NSF | ASTM D2000 M1GE505 | 50 ± 5 | 930 | Volume change, +59% | 61% | Yes | |
![]() |
6604-NSF | ASTM D2000 M1GE605 | 60 ± 5 | 925 | Volume change, +46% | 33% | Yes | |
![]() |
6704-NSF | ASTM D2000 M1GE705 | 70 ± 5 | 820 | Volume change, +41% | 42% | Yes | |
![]() |
6804-NSF | ASTM D2000 M1GE805 | 80 ± 5 | 810 | Volume change, +35% | 40% | Yes |
Bellofram Dense Solid Silicone - Molded
MATERIAL PROPERTIES OF BELLOFRAM SILICONES HIGH TEAR AND FLEX RESISTANT SOLID SILICONE MOLDED PRODUCTS | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
SOLID SILICONE MOLDED PRODUCTS TO SPEC TO SPEC A-A-59588 CL3B, GR30, GR50 | ASTM D395 | Heat Age, 70 Hours @ +200°C (ASTM D573) | ASTM D2137 | ASTM D471 | ASTM D813 | ASTM D2632 | |||||||
SPEC SHEET DOWNLOAD | COMPOUND MODEL | DUROMETER, SHORE "A" | TENSILE STRENGTH min MPa (psi) | ELONGATION % min. | TEAR RESISTANCE, kN/m (ppi) | COMPRESSION SET, 70 Hours @ +100°C | HARDNESS CHANGE | TENSILE CHANGE | ELONGATION CHANGE | BRITTLE POINT, min. °C (°F) | WATER IMMERSION, VOLUME CHANGE % | DeMATTIA FLEX, (1/2 inch max crack growth) | IMPACT RESILIENCE, min % |
![]() |
8305 | 30 ± 5 | 6.9 (1000) | 500 | 26.25 (150) | 25 | ± 5 | -20% | -35% | -70 (-94) | +5 | 500,000 cycles | 40 |
![]() |
8505 | 50 ± 5 | 8.28 (1200) | 500 | 26.25 (150) | 20 | ± 10 | -25% | -30% | -70 (-94) | +5 | 140,000 cycles | 45 |
Solid silicone molded products
MATERIAL PROPERTIES OF BELLOFRAM SILICONES SOLID SILICONE MOLDED PRODUCTS | |||||||
SPEC SHEET DOWNLOAD | COMPOUND MODEL | ASTM D2000-08 DESIGNATION | DUROMETER SHORE "A" | TENSILE (PSI) | HEAT AGE, 70 Hours @ +225 °C | OIL IMMERSION IRM 903 70 hrs @+150 °C | COMPRESSION SET, 22 Hours @ +175°C |
![]() |
8304 | ASTM D2000 M1GE305 | 30 ± 5 | 1350 | Change in Tensile Strength, ±30% Change in Elongation, -50% Change in Durometer, ±15 pts | Volume change, +64% | 14% |
![]() |
8404 | ASTM D2000 M1GE405 | 40 ± 5 | 1235 | Volume change, +62% | 16% | |
![]() |
8504 | ASTM D2000 M1GE505 | 50 ± 5 | 1100 | Volume change, +49% | 18% | |
![]() |
8604 | ASTM D2000 M1GE605 | 60 ± 5 | 725 | Volume change, +47% | 26% | |
![]() |
8704 | ASTM D2000 M1GE705 | 70 ± 5 | 900 | Volume change, +38% | 28% | |
![]() |
8804 | ASTM D2000 M1GE805 | 80 ± 5 | 1000 | Volume change, +30% | 23% |
MATERIAL PROPERTIES OF BELLOFRAM FLAME RETARDANT SOLID SILICONE MOLDED PRODUCTS | ||||||||
SPEC SHEET DOWNLOAD | COMPOUND MODEL | ASTM D2000-08 DESIGNATION | DUROMETER SHORE "A" | TENSILE (PSI) | HEAT AGE, 70 Hours @ +225 °C | OIL IMMERSION IRM 903 70 hrs @ +150°C | COMPRESSION SET, 22 hrs @+175°C | MEETS BURN REQUIREMENTS OF UL 94 V-0 |
![]() |
8309 | ASTM D2000 M1GE305 | 30 ± 5 | 1350 | Change in Tensile Strength, ±30% Change in Elongation, -50% Change in Durometer, ±15 pts | Volume change, +64% | 14% | PASS |
![]() |
8409 | ASTM D2000 M1GE405 | 40 ± 5 | 1235 | Volume change, +62% | 16% | PASS | |
![]() |
8509 | ASTM D2000 M1GE505 | 50 ± 5 | 1100 | Volume change, +49% | 18% | PASS | |
![]() |
8609 | ASTM D2000 M1GE605 | 60 ± 5 | 725 | Volume change, +47% | 26% | PASS | |
![]() |
8709 | ASTM D2000 M1GE705 | 70 ± 5 | 900 | Volume change, +38% | 28% | PASS | |
![]() |
8809 | ASTM D2000 M1GE805 | 80 ± 5 | 1000 | Volume change, +30% | 23% | PASS |
MATERIAL PROPERTIES OF BELLOFRAM NSF/ANSI 51 COMPLIANT SOLID SILICONE MOLDED PRODUCTS | ||||||||
SPEC SHEET DOWNLOAD | COMPOUND MODEL | ASTM D2000-08 DESIGNATION | DUROMETER SHORE "A" | TENSILE (PSI) | HEAT AGE, 70 Hours @ +225 °C | OIL IMMERSION IRM 903 70 hrs @ +150 °C | COMPRESSION SET, 22 Hrs @+175°C | NSF/ANSI 51 CERTIFIED |
![]() |
8304-NSF | ASTM D2000 M1GE305 | 30 ± 5 | 1350 | Change in Tensile Strength, ±30% Change in Elongation, -50% Change in Durometer, ±15 pts | Volume change, +64% | 14% | YES |
![]() |
8404-NSF | ASTM D2000 M1GE405 | 40 ± 5 | 1235 | Volume change, +62% | 16% | YES | |
![]() |
8504-NSF | ASTM D2000 M1GE505 | 50 ± 5 | 1100 | Volume change, +49% | 18% | YES | |
![]() |
8604-NSF | ASTM D2000 M1GE605 | 60 ± 5 | 725 | Volume change, +47% | 26% | YES | |
![]() |
8704-NSF | ASTM D2000 M1GE705 | 70 ± 5 | 900 | Volume change, +38% | 28% | YES | |
![]() |
8804-NSF | ASTM D2000 M1GE805 | 80 ± 5 | 1000 | Volume change, +30% | 23% | YES |